The effect of decalin and perfluorodecalin on Dendrite formation at metal lithium anodes During their operation

Capa

Citar

Texto integral

Acesso aberto Acesso aberto
Acesso é fechado Acesso está concedido
Acesso é fechado Acesso é pago ou somente para assinantes

Resumo

In this work, we studied the effect of additions of decahydronaphthalene (decalin) and its derivative, perfluorodecalin (octadecafluorodecalin), on the deposition and dissolution of lithium metal, including dendrite formation, at the anodes of secondary lithium power sources in an electrolyte based on lithium hexafluorophosphate and a mixture of ethylene carbonate (EC) and diethyl carbonate (DEC). The study was carried out using the methods of current transients and electrochemical impedance. The results showed that, in contrast to traditional cationic surfactants cetyltrimethylammonium bromide and hexadecylpyridinium bromide, which we studied earlier, decalin and perfluorodecalin demonstrate specific interaction with the surface of the lithium electrode. Moreover, the interaction with decalin is so strong that it actually blocks the processes of both deposition and anodic dissolution of lithium at the surface of the lithium electrode. The interaction of perfluorodecalin with the lithium surface turned out to be weaker. As a result, perfluorodecalin does not interfere with the cycling of the metal lithium anode, but at the same time shows an inhibitory effect on the dendrite formation. In the electrolyte with the addition of perfluorodecalin, lithium anode was able to undergo more than 80 charge-discharge cycles with a Coulomb efficiency of 70–80%, while without the additive, the number of cycles was less than 40, and the Coulomb efficiency was 60% or lower.

Texto integral

Acesso é fechado

Sobre autores

S. Alpatov

M.V. Lomonosov Moscow State University

Email: osemenik@elch.chem.msu.ru

Department of Chemistry

Rússia, Moscow

F. Vasiliev

M.V. Lomonosov Moscow State University

Email: osemenik@elch.chem.msu.ru

Department of Chemistry

Rússia, Moscow

O. Semenikhin

M.V. Lomonosov Moscow State University

Autor responsável pela correspondência
Email: osemenik@elch.chem.msu.ru

Department of Chemistry

Rússia, Moscow

Bibliografia

  1. Алпатов, С. С., Васильев, Ф. А., Алешина, В. Х., Ваграмян, Т. А., Семенихин, О. А. Электроосаждение лития в присутствии поверхностно-активных веществ. Электрохимия. 2024. Т. 60. № 5. С. 349.
  2. Алпатов, С. С., Васильев, Ф. А., Алешина, В. Х., Ваграмян, Т. А., Семенихин, О. А. Анализ спектров электрохимического импеданса и строения твердоэлектролитной интерфазы на электроосажденном металлическом литии с использованием метода распределения времен релаксации. Электрохимия. 2024. Т. 60. № 5. С. 361.
  3. Chen, S.R., Dai, F., and Cai, M., Opportunities and Challenges of High-Energy Lithium Metal Batteries for Electric Vehicle Applications, ACS Energy Lett., 2020, vol. 5, p. 3140.
  4. Liu, D.H., Bai, Z.Y., Li, M., Yu, A.P., Luo, D., Liu, W.W., Yang, L., Lu, J., Amine, K., and Chen, Z.W., Developing high safety Li-metal anodes for future high-energy Li-metal batteries: strategies and perspectives, Chem. Soc. Rev., 2020, vol. 49, p. 5407.
  5. Qin, K., Holguin, K., Mohammadiroudbari, M., Huang, J., Kim, E. Y. S., Hall, R., and Luo, C., Strategies in structure and electrolyte design for high-performance lithium metal batteries, Adv. Funct. Mater., 2021, vol. 31, p. 2009694.
  6. Besenhard, J.O., Gürtler, J., Komenda, P., and Paxinos, A., Corrosion protection of secondary lithium electrodes in organic electrolytes, J. Power Sources, 1987, vol. 20, p. 253.
  7. von Aspern, N., Roeschenthaler, G.-V., Winter, M., and Cekic-Laskovic, I., Fluorine and Lithium: Ideal Partners for High-Performance Rechargeable Battery Electrolytes, Angew. Chem. Int. Ed., 2019, vol. 58, p. 16124.
  8. Xu, N., Shi, J., Liu, G., Yang, X., Zheng, J., Zhang, Z., and Yang, Y., Research progress of fluorine-containing electrolyte additives for lithium ion batteries, J. Power Sources Adv., 2021, vol. 7, p. 100043.
  9. Scharifker, B. and Hills, G., Theoretical and experimental studies of multiple nucleation, Electrochim. Acta, 1983, vol. 28, p. 879.
  10. Scharifker, B.R., Mostany, J., Palomar‐Pardavé, M., and González, I., On the theory of the potentiostatic current transient for diffusion‐controlled three‐dimensional electrocrystallization processes, J. Electrochem. Soc., 1999, vol. 146, p. 1005.

Arquivos suplementares

Arquivos suplementares
Ação
1. JATS XML
Baixar
2. Fig. 1. Impedance hodographs measured on electrodes made of (a) lithium and (b) copper before deposition of metallic lithium at a potential of –0.03 V in the presence of additives of (1) perfluorinated and (2) non-fluorinated decalin.

Baixar (140KB)
Metadados
3. Fig. 2. Impedance hodographs measured on electrodes made of (a) lithium and (b) copper after deposition of metallic lithium at a potential of –0.03 V in the presence of additives of (1) perfluorinated and (2) non-fluorinated decalin.

Baixar (122KB)
Metadados
4. Fig. 3. Current density transients measured during the deposition of metallic lithium on (a) copper and (b) lithium electrodes at a potential of –0.03 V in the following electrolytes: (1) with the addition of decalin, (2) with the addition of perfluorodecalin, (3) without additives.

Baixar (137KB)
Metadados
5. Fig. 4. Current density transients measured during lithium metal deposition: (a, b) on the copper electrode in the electrolyte with the addition of decalin, (c) on the copper electrode in the electrolyte with the addition of perfluorodecalin, (d) on the lithium electrode in the electrolyte with the addition of decalin (curves 1, 2) and with the addition of perfluorodecalin (curves 3, 4, 5). Potentials: (a, b) 1 – –0.03 V, 2 – –0.025 V, 3 – –0.04 V, 4 – –0.6 V, 5 – –0.1 V; (c) 1 – –0.03 V, 2 – –0.06 V, 3 – –0.095 V; (d) 1 – –0.085 V, 2 – –0.06 V, 3 – –0.03 V, 4 – –0.06 V, 5 – –0.1 V.

Baixar (272KB)
Metadados
6. Fig. 5. Galvanostatic charge-discharge curves obtained for galvanostatic deposition-dissolution of lithium on a copper electrode at a current density of 0.1 mA/cm² (1) in a standard electrolyte without additives and (2) in an electrolyte with the addition of perfluorinated decalin. Cycle No. 7.

Baixar (81KB)
Metadados

Declaração de direitos autorais © Russian Academy of Sciences, 2024