Investigation of the influence of mechanical activation time on the formation the Ni3Al-based high alloys obtained by spark plasma sintering

封面

如何引用文章

全文:

开放存取 开放存取
受限制的访问 ##reader.subscriptionAccessGranted##
受限制的访问 订阅存取

详细

Compacts obtained because of different times of mechanical activation of mixtures corresponding to alloys of VKNA-1V and VKNA-4U grades, with subsequent spark plasma sintering, were studied. The maximum level of tensile strength of compact materials of VKNA-1V is 1200 MPa, and for the VKNA-4U is 1100 MPa, and was achieved after 3.5 minutes of mechanical activation.

全文:

受限制的访问

作者简介

L. Shevtsova

Novosibirsk State Technical University

编辑信件的主要联系方式.
Email: edeliya2010@mail.ru
俄罗斯联邦, Novosibirsk

M. Esikov

Novosibirsk State Technical University; Lavrentyev Institute of Hydrodynamics of the Siberian Branch of the Russian Academy of Sciences

Email: edeliya2010@mail.ru
俄罗斯联邦, Novosibirsk; Novosibirsk

A. Gavrilov

Institute of Solid State Chemistry and Mechanochemistry of the Siberian Branch of the Russian Academy of Sciences

Email: edeliya2010@mail.ru
俄罗斯联邦, Novosibirsk

E. Lojkina

Novosibirsk State Technical University

Email: edeliya2010@mail.ru
俄罗斯联邦, Novosibirsk

D. Shevtsov

Novosibirsk State Technical University

Email: edeliya2010@mail.ru
俄罗斯联邦, Novosibirsk

Ya. Merzlikina

Novosibirsk State Technical University

Email: edeliya2010@mail.ru
俄罗斯联邦, Novosibirsk

参考

  1. Ночовная Н.А., Базылева О.А., Каблов Д.Е., Панин П.В. Интерметаллидные сплавы на основе титана и никеля. М: ВИАМ, 2018.
  2. Mardiha P., Bahrami A., Mohammadnejad A. // Sci. Sinter. 2019. V. 51. P. 401.
  3. Frage N., Kalabukhov S., Wagner A., Zaretsky E.B. // Intermetal. 2018. V. 102. P. 26.
  4. Bazyleva O.A., Efimochkin I.Y., Arginbaeva E.G. et al. // Inorg. Mater. Appl. Res. 2021. V. 12. P. 307.
  5. Шевцова Л.И. // Металлург. 2023. № 8. С. 63; Shevtsova L.I. // Metallurgist. 2023. V. 67. P. 1146.
  6. Ковалевская Т.А., Данейко О.И. // Изв. РАН. Сер. физ. 2021. Т. 85. № 7. С. 776; Kovalevskaya T.A., Daneyko O.I. // Bull. Russ. Acad. Sci. Phys. 2021. V. 85. No. 7. P. 776.
  7. Шкодич Н.Ф., Кочетов Н.А., Рогачев А.С. и др. // Изв. РАН. Сер. физ. 2007. Т. 71. № 5. С. 650; Shkodich N.F., Kochetov N.A., Rogachev A.S. et al. // Bull. Russ. Acad. Sci. Phys. 2007. V. 71. No. 5. P. 650.
  8. Шевцова Л.И., Корчагин М.А., Есиков М.А. и др. // Металлург. 2021. № 11. С. 56. Shevtsova L.I., Korchagin M.A., Esikov M.A. et al. // Metallurgist. 2022. No. 65. No. 11–12. P. 1273.
  9. Собачкин А.В., Логинова М.В., Ситников А.А. и др. // Изв. РАН. Сер. физ. 2023. Т. 87. № 5. С. 629; Sobachkin A.V., Loginova M.V., Sitnikov A.A. et al. // Bull. Russ. Acad. Sci. Phys. 2023. V. 87. No. 5. P. 629.
  10. Жежу М., Васильев А.Е., Иванов О.Н. // Изв. РАН. Сер. физ. 2023. Т. 87. № 6. С. 687; Zhezhu M., Vasil'ev A.E., Ivanov O.N. // Bull. Russ. Acad. Sci. Phys. 2023. V. 87. No. 6. P. 687.
  11. Каблов Е.Н., Оспенникова О.Г., Базылева О.А. // Вестн. МГТУ им. Н. Э. Баумана. Сер. машиностр. 2011. № SP2. С. 13.
  12. Тюменцев А.Н., Дитенберг И.А., Корчагин М.А. // ФММ. 2011. Т. 111. № 2. С. 195.
  13. Осипов Д.А. Микроструктура и физико-механические свойства сплавов на основе Ni3Al в зависимости от условий предварительной обработки прекурсоров и синтеза. Автореферат дисс. … канд. физ.-мат. наук. Томск, 2023. 29 с.
  14. Шевцова Л.И., Есиков М.А., Малютина Ю.Н. и др. // Письма в ЖТФ. 2024. Т. 50. № 2. С. 3.
  15. Бунтушкин В.П., Базылева О.А., Буркина В.И. // Авиац. матер. и технол. 2015. № 1. С. 34.
  16. Оспенникова О.Г., Базылева О.А., Евгенов А.Г. и др. // Авиац. матер. и технол. 2016. № 1. С. 36.

补充文件

附件文件
动作
1. JATS XML
下载
2. Fig. 1. X-ray diffraction patterns of reaction mixtures of the composition VKNA-1V (a, b); VKNA-4U (c) mechanically activated at different times. Morphology of the mechanocomposite of the composition VKNA-4U after 3.5 min of MA.

下载 (58KB)
索引源数据
3. Fig. 2. Structure of materials of the composition VKNA-1V and VKNA-4U sintered in different SPS modes. Optical microscopy.

下载 (76KB)
索引源数据
4. Fig. 3. Structure of the VKNA-4U alloy sintered by the SPS method at 1150 °C and 40 MPa (a–c) and the results of X-ray spectral microanalysis (d, e). Scanning electron microscopy.

下载 (66KB)
索引源数据
5. Fig. 4. Curve (σ – ε) of tensile deformation at a test temperature of 20 °C for the alloy VKNA-1V (curve 1) and VKNA-4U (curve 2), obtained by the SPS method at 60 MPa (a). Fractograms after uniaxial tensile testing of VKNA-1V (b); VKNA-4U (c) alloy sintered at 60 MPa.

下载 (66KB)
索引源数据

版权所有 © Russian Academy of Sciences, 2024